| Customization: | Available |
|---|---|
| Raw Material: | Silicone Rubber |
| Material: | Silicone Rubber |
|
Still deciding? Get samples of US$ 5/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Two-component silicone, tin-curing, flowable, vulcanizes at room temperature.
Can be used for a long time in the temperature range of - 65 ° C - 200 ° C and keep its soft and elastic properties.
General mold making.
Suitable for reproducing and replicating products in large quantity for industries: Art crafts, sculptures, furniture, architectural elements, garden ornaments, tire, soap, candle and so on. Used for making molds for variety of material, such as resin, PU, gypsum, plaster, concrete, cement, stone, GRC, PVC, polyester, wax, bronze and so on.
Tin/condensation cure silicone rubber
Base and Curing Agent Mixture (100:3 by weight) in 25 °C (77F) testing
| Item | Mixing Ratio | Color |
Hardness (shore A) |
Viscosity (mPa.s) | Working Time (25ºC) | Curing Time (25ºC) | Tear-Strength (kN/m) | Tensile- Strength (Mpa) | Elongation (%) | Shrinkage(%) |
| OTT-S805 | 100:3 | white or translucent | 5±2 |
5000±2000 |
20-40mins | 3-5h | ≥10 | ≥1.6 | ≥500 | ≤0.2 |
| OTT-S810 | 100:3 | white or translucent | 10±2 | 8000±2000 | 20-40mins | 3-5h | ≥16 | ≥3.2 | ≥600 | ≤0.2 |
| OTT-S815 | 100:3 | white or translucent | 15±2 | 11000±3000 | 20-40mins | 3-5h | ≥24 | ≥3.5 | ≥580 | ≤0.2 |
| OTT-S820 | 100:3 | white or translucent | 20±2 | 11000±3000 | 20-40mins | 3-5h | ≥23 | ≥4.2 | ≥500 | ≤0.2 |
| OTT-S825 | 100:3 | white or translucent | 25±2 | 16000±3000 | 20-40mins | 3-5h | ≥26 | ≥4.5 | ≥500 | ≤0.2 |
| OTT-S830 | 100:3 | white or translucent | 30±2 | 21000±3000 | 20-40mins | 3-5h | ≥26 | ≥4.5 | ≥450 | ≤0.2 |
| OTT-S835 | 100:3 | white or translucent | 35±2 | 18000±3000 | 20-40mins | 3-5h | ≥24 | ≥4.2 | ≥350 | ≤0.2 |
| OTT-S840 | 100:3 | white or translucent | 40±2 | 12000±3000 | 20-40mins | 3-5h | ≥22 | ≥4.0 | ≥280 | ≤0.2 |
Addtion/platinum cure silicone rubber
Base and Curing Agent Mixture (1:1 by weight) in 25 °C (77F) testing
| Item | Mixing Ratio | Color | Hardness(shore A) | Viscosity (mPa.s) | Working Time (25ºC) | Curing Time (25ºC) | Tear-Strength (kN/m) | Tensile- Strength (Mpa) | Elongation (%) | Shrinkage(%) |
| OTT-J805 | 1:1 | translucent | 5±2 | 1500±500 | 20-40mins | 3-5h | ≥12 | ≥2.2 | ≥500 | ≤0.1 |
| OTT-J810 | 1:1 | translucent | 10±2 | 2000±1000 | 20-40mins | 3-5h | ≥15 | ≥4.2 | ≥450 | ≤0.1 |
| OTT-J815 | 1:1 | translucent | 15±2 | 3000±1000 | 20-40mins | 3-5h | ≥18 | ≥5.2 | ≥450 | ≤0.1 |
| OTT-J820 | 1:1 | translucent | 20±2 | 4500±2000 | 20-40mins | 3-5h | ≥24 | ≥5.2 | ≥500 | ≤0.1 |
| OTT-J825 | 1:1 | translucent | 25±2 | 5000±2000 | 20-40mins | 3-5h | ≥22 | ≥6.2 | ≥500 | ≤0.1 |
| OTT-J830 | 1:1 | translucent | 30±2 | 6000±2000 | 20-40mins | 3-5h | ≥21 | ≥6.5 | ≥450 | ≤0.1 |
| OTT-J835 | 1:1 | translucent | 35±2 | 6000±2000 | 20-40mins | 3-5h | ≥22 | ≥6.5 | ≥450 | ≤0.1 |
| OTT-J840 | 1:1 | translucent | 40±2 | 7000±2000 | 20-40mins | 3-5h | ≥18 | ≥7.8 | ≥450 | ≤0.1 |
| OTT-J850 | 1:1 | translucent | 50±2 | 8000±3000 | 20-40mins | 3-5h | ≥12 | ≥7.0 | ≥400 | ≤0.1 |
){kind=link}